Yuhong Holding Group Co.,LTD
 |
| Place of Origin: | China, USA, Korea, UE |
| Brand Name: | YUHONG SPECIAL STEEL |
| Certification: | ABS, GL, DNV, NK, PED, AD2000, GOST9941-81, CCS, ISO 9001-2008 |
| Model Number: | A213 TP347/347H , A312 TP347H, A269 TP347H |
| Minimum Order Quantity: | 1PC |
|---|---|
| Price: | Negotiable |
| Packaging Details: | Ply-wooden Case /Iron Case/ Bundle with plastic Cap |
| Delivery Time: | 5-80 Days |
| Payment Terms: | T/T, L/C |
| Supply Ability: | 1500 tons per month |
| Application: | Industrial, Construction, Decoration | Length: | Customized |
|---|---|---|---|
| Material: | Stainless Steel | Package: | Standard Export Package |
| Payment Term: | T/T, L/C, Western Union, Paypal | Port: | Shanghai, Ningbo, Qingdao, Tianjin, Guangzhou, Shenzhen |
| Processing Technology: | Cold Drawn, Cold Rolled, Hot Rolled | Shape: | Seamless Tube |
| Size: | Customized | Standard: | ASTM, DIN, JIS, GB, EN, BS, AISI |
| Surface Treatment: | Polishing, Anodizing, Sandblasting, Coating | Wall Thickness: | Customized |
| High Light: | seamless stainless steel tube,stainless steel seamless pipes |
||
ASTM A213/ASME SA213 347H Stainless Steel Seamless Tubes for Automotive Industry
Product Range
Specifications: ASTM/ASME A213
Sizes (Seamless): 1/2" NB - 24" NB
Sizes (ERW): 1/2" NB - 24" NB
Sizes (EFW): 6" NB - 100" NB
Wall Thickness available:
Schedule 5S - Schedule XXS (heavier on request)
Other Materials Testing:
NACE MR0175, H2 SERVICE, OXYGEN SERVICE, CRYO SERVICE, etc.
Dimensions:
All Pipes is manufactured and inspected/tested to the relevant standards including ASTM, ASME and API etc.
General Properties of 347H Stainless Steel Pipes
The general properties of 347H stainless steel pipes are similar to those of 347H stainless steel tubes, as they both belong to the same alloy. Here are some key properties of 347H stainless steel pipes:
1. Corrosion resistance: 347H stainless steel pipes offer excellent resistance to corrosion in various environments, including acidic, alkaline, and chloride-containing solutions. They have a high resistance to intergranular corrosion due to the addition of niobium.
2. Heat resistance: These pipes have good high-temperature strength and can withstand elevated temperatures up to 1000°C (1832°F). They are commonly used in applications involving intermittent heating and cooling cycles.
3. Weldability: 347H stainless steel pipes can be easily welded using conventional welding methods. They offer good weldability and can be welded without the risk of intergranular corrosion.
4. Mechanical properties: The mechanical properties of 347H stainless steel pipes include high tensile strength, good yield strength, and excellent toughness. They exhibit good ductility and can be formed into various shapes.
5. Machinability: 347H stainless steel pipes have good machinability. They can be easily machined using conventional methods, although the presence of high carbon content may reduce tool life.
6. Physical properties: The density of 347H stainless steel pipes is around 7.96 g/cm³. They have a melting point of approximately 1454°C (2650°F) and a thermal conductivity of 16.3 W/m·K.
Specific properties may vary depending on the manufacturer and the specific grade of 347H stainless steel pipes. It is recommended to consult the manufacturer's datasheet or technical specifications for more accurate and detailed information.
Chemical Composition of 347H Stainless Steel Tubes
The chemical composition of grade 347 Stainless Steel is outlined in the following table
| Element | 347 | 347H |
| Chromium | 17.00 min.-19.00 max. | 17.00 min.-19.00 max. |
| Nickel | 9.00 min.-13.00 max. | 9.00 min.-13.00 max. |
| Carbon | 0.08 | 0.04 min.-0.10 max. |
| Manganese | 2.00 | 2.00 |
| Phosphorus | 0.045 | 0.045 |
| Sulfur | 0.03 | 0.03 |
| Silicon | 0.75 | 0.75 |
| Columbium & Tantalum | 10 x (C + N) min.-1.00 max. | 8 x (C + N) min.-1.00 max. |
| Iron | Balance | Balance |
The Mechanical Properties of grade 347H Stainless Steel Typical Values at 68°F (20°C) are displayed in the following table
| Yield Strength 0.2% Offset |
Ultimate Tensile Strength |
Elongation in 2 in. |
Hardness | ||
| psi (min.) | (MPa) | psi (min.) | (MPa) | % (min.) | (max.) |
| 30,000 | 205 | 75,000 | 515 | 40 | 201 Brinell |
ASTM A213 TP347H Stainless Steel Seamless Pipes Physical Properties
Physical properties of 347H grade stainless steel in the annealed condition
| Properties | Metric |
| Density | 7.96 g/cm3 |
Heat Treatment of 347H Stainless Steel Pipes
The heat treatment of 347H stainless steel pipes is similar to that of 347H stainless steel tubes. The most common heat treatment processes for 347H stainless steel pipes include annealing and solution annealing.
1. Annealing: Annealing is typically performed by heating the pipes to a temperature range of 1010°C to 1120°C (1850°F to 2050°F) and then slowly cooling them in a furnace or air. This process helps to soften the material, improve ductility, and relieve any residual stresses from previous processing operations.
2. Solution Annealing: Solution annealing is commonly performed on pipes that have been cold-worked or welded. It involves heating the pipes to a temperature range of 1010°C to 1120°C (1850°F to 2050°F) for a sufficient period of time, followed by rapid quenching in water or oil. This process helps to dissolve any carbides that may have formed during cold-working or welding, restoring the material's corrosion resistance and mechanical properties.
After the heat treatment process, the pipes may undergo further processing steps such as pickling, passivation, and/or cold-working to achieve the desired final dimensions and surface finish.
It is important to note that the specific heat treatment process and parameters may vary depending on the manufacturer's recommendations, the specific grade of 347H stainless steel, and the intended application of the pipes. It is recommended to consult the manufacturer's technical specifications or guidelines for the appropriate heat treatment for your specific requirements.
Typical Uses
Due to their excellent corrosion resistance and heat resistance, 347H stainless steel pipes are widely used in various industries, including chemical processing plants, oil and gas refineries, power generation, and other high-temperature applications.
Applications