| Standard: | ASME SB167 | Material: | Inconel 601 |
|---|---|---|---|
| Application: | For Fluid And Gas Transport | Shape: | Round Pipe |
| Technique: | Cold Drawn/ Cold Rolled | NDT: | Eddy Current Or Hydraulic Test |
| High Light: | inconel 601 Nickel Alloy Pipe,ASME SB167 Nickel Alloy Pipe,inconel 601 nickel alloy tubes |
||
Astm b167 inconel 601 / asme sb167 nickel alloy 601 tubes
We are one of the biggest manufactures of stainless steel & duplex steel & alloy steel tubes and pipes in China. With development more than 20 years, we have accumulated a great many clients all around the world and Yuhong products also won the great praise among the customers.
INCONEL nickel-chromium-iron alloy 601 (UNS N06601/W.Nr. 2.4851) is a general-purpose engineering material for applications that require resistance to heat and corrosion. An outstanding characteristic of INCONEL alloy 601 is its resistance to hightemperature oxidation. The alloy also has good resistance to aqueous corrosion, has high mechanical strength, and is readily formed, machined and welded.
The most important property of Inconel 601 is resistance to oxidation at very high temperatures up to 1250C. Even under severe conditions such as, cyclical heating and cooling. This is possible due to Inconel 601 having a tightly adherent oxide layer which is resistant against spalling. Resistance to carburization is good, also resistant to carbon nitriding conditions. Due to high chromium and some aluminum content, good resistance in oxidizing sulfur bearing atmospheres at elevated temperatures is demonstrated.
Application
Physical Properties
| Density | 8.1 g/cm cube |
| Specific Heat | 461 J/kg K |
| Electrical Resistivity | 119 micro ohms cm |
| Curie Temperature | -190 C |
| Melting Range | 1320 - 1370 C |
| Thermal Expansion(10-6K) | 14.9 (20-300 C) |
Chemical Composition
| Element | % |
| Nickel | 58.0-63.0 |
| Chromium | 21.0-25.0 |
| Iron | ~ 16 |
| Aluminium | 1.0-1.7 |
| Carbon | 0.10 max |
| Manganese | 1.5 max |
| Silicon | 0.50 max |
| Sulphur | 0.015 max |
| Copper | 1.0 max |
Mechanical Properties
| 0.2% Proof Stress | Tensile Strength | Elongation |
| MPa | MPa | % |
| 205 | 550 | 30 |
Heat Treatment
Inconel 601 is solution annealed at 1100 – 1180°C, and cooled quickly so as to avoid sensitisation to intergranular corrosion. Annealing time should be short to avoid excessive grain growth.
Corrosion Resistance
Inconel 601 has excellent corrosion resistance to the mineral acids, similar to Inconel 600. Inconel 601 has good resistance to sodium hydroxide solutions and because of the high nickel content good resistance to chloride stress corrosion cracking. As with austenitic stainless steels Inconel 601 can be sensitised to intergranular corrosion in some aggressive media after heating in the temperature range 540 – 760°C. Please consult Austral Wright Metals for your specific application.