Yuhong Holding Group Co.,LTD
Place of Origin: | China |
Brand Name: | YUHONG |
Certification: | ABS, GL, DNV, NK, PED, AD2000, GOST9941-81, CCS, ISO 9001-2008 |
Model Number: | ASTM B111/ASME SB111 C68700 U-TUBE |
Minimum Order Quantity: | 100KGS |
---|---|
Price: | Negotiable |
Packaging Details: | Ply-wooden Case /Iron Case/ Bundle with plastic Cap |
Delivery Time: | 15-30 days |
Payment Terms: | T/T, L/C AT SIGHT |
Supply Ability: | 100 tons per month |
Material: | C68700 Aluminum Brass | Application: | Boiler, Superheater, Heat-Exchanger, And Condenser Tubes |
---|---|---|---|
Technique: | Cold Drawn | Standard: | ASTM,ASME |
Usage: | Heat Exchanger/Boiler | Shape: | U-Shape |
High Light: | astm b111 u bend tube,c68700 u bend tube,b111m u bend tube |
Overview
ASTM B111 C68700 Aluminum Brass tube, UNS CDA01, ASTM B111, ASTM B395, ASTM B187, ASTM B152. ASTM B111 C68700 has especially good corrosion resistance properties in sea water. Aluminum Brass Tube is a copper zinc alloy containing aluminum and small amount of arseric which is added as an inhibitor against dezincification. Inhibited Aluminum Brass resists the action of high velocity salt and brackish water and is commonly used for condenser tube. The outstanding characteristic of Aluminum Brass is the high resistance to impringement attack. Aluminum Brass tubes are highly accepted and one of the extensively used material for various industrial applications.
Specification
ASTM B111/B111M Standard Specification for Copper and Copper-Alloy Seamless Tubes
Standard Grade | ASTM B111 C68700 | EN 12451 CuZn20Al2As | DIN 17660/1785 CuZn20Al2 | BS 2871 CZ 110 | JIS H3300 C6870 | GB/T 8890 HAL 77-2 |
Cu | 76.0-79.0 | 76.0-79.0 | 76.0-79.0 | 76.0-78.0 | 76.0-79.0 | 76.0-79.0 |
Al | 1.8-2.5 | 1.8-2.3 | 1.8-2.3 | 1.8-2.3 | 1.8-2.5 | 1.8-2.5 |
Fe | 0.06 max | 0.07 max | 0.07 max | 0.06 max | 0.06 max | 0.06 max |
Pb | 0.07 max | 0.05 max | 0.07 max | 0.07 max | 0.07 max | 0.03 max |
Zn | Bal. | Bal. | Bal. | Bal. | Bal. | Bal. |
As | 0.02-0.10 | 0.02-0.06 | 0.02-0.035 | 0.02-0.06 | 0.02-0.06 | 0.03-0.06 |
P | - | 0.01 max | 0.01 max | - | - | 0.02 max |
Mn | - | 0.1 max | 0.1 max | - | - | - |
Total Impurities | - | 0.3 max | 0.1 max | 0.3 max | - | 0.3 max |
Condition | O61 | R390 | F39 | M | O | M |
- | R340 | F34 | TA | - | Y2 | |
- | - | - | O | - | - | |
Yield Strength N/mm2 | 125 min | 150 min | 150-230 | - | - | - |
- | 120 min | 120-180 | - | - | - | |
- | - | - | - | - | - | |
Tensile trength N/mm2 | 345 min. | 390 min | - | - | 373 min | 370min |
- | 340 min | - | - | - | 350 min | |
- | - | - | - | - | - | |
Elongation (%) | - | 45 min | 45 min | - | 40 min | 40 min |
- | 55 min | 55 min | - | - | 50 min | |
- | - | - | - | - | - | |
Hardness Hv5 | - | - | - | 150 min | - | - |
- | - | - | 85-110 | - | - | |
- | - | - | 75 max | - | - |
Elements | ||||||
---|---|---|---|---|---|---|
Cu(1,2) | Pb | Zn | Fe | Al | As | |
(1) Cu value includes Ag.
|
||||||
Min (%) | 76.0 | 1.8 | 0.02 | |||
Max (%) | 79.0 | 0.07 | Rem | 0.06 | 2.5 | 0.06 |
Form | Temper | Temper Code | Tensile Strength (ksi) |
YS-0.5% Ext (ksi) |
Elongation (%) |
Rockwell F scale |
---|---|---|---|---|---|---|
*Measured at room temperature, 68°F (20°C).
|
||||||
Tube | Nominal Grain Size 0.025 mm | OS025 | 60 Typ | 27 Typ | 55 Typ | 77 Typ |
Melting Point - Liquidus°F | 1780 |
---|---|
Melting Point - Solidus°F | 1710 |
Densitylb/cu in. at 68°F | 0.301 |
Specific Gravity | 8.33 |
Electrical Conductivity% IACS at 68°F | 23 |
Thermal ConductivityBtu/ sq ft/ ft hr/ °F at 68°F | 58 |
Coefficient of Thermal Expansion 68-57210 to -6 power per °F (68 – 572°F) | 10.3 |
Specific Heat CapacityBtu/ lb /°F at 68°F | 0.09 |
Modulus of Elasticity in Tensionksi |
16000 |
Modulus of Rigidityksi |
6000 |
Technique | Suitability |
---|---|
Soldering | Fair |
Brazing | Good |
Oxyacetylene Welding | Fair |
Gas Shielded Arc Welding | Fair |
Coated Metal Arc Welding | Not Recommended |
Spot Weld | Good |
Seam Weld | Fair |
Butt Weld | Good |
Capacity for Being Cold Worked | Excellent |
Capacity for Being Hot Formed | Fair |
Machinability Rating | 30 |