Yuhong Holding Group Co.,LTD
Place of Origin: | CHINA |
Brand Name: | YUHONG |
Certification: | ABS, GL, DNV, NK, PED, AD2000, GOST9941-81, CCS, ISO 9001-2008 |
Model Number: | ASTM A182 F904L |
Minimum Order Quantity: | 100 KGS |
---|---|
Price: | NEGOTIABLE |
Packaging Details: | Ply-wooden Case /Iron Case/ Bundle with plastic Cap |
Delivery Time: | 20-80 days |
Payment Terms: | T/T, L/C, Western Union |
Supply Ability: | 1500 Tons Per Month |
Standard: | DIN, ANSI, ISO, ASME, JIS | Size: | 15mm-6000mm, STD, 1/2"-120", DN 10-DN3000 |
---|---|---|---|
Material: | Stianless Steel | Product Name: | Long Welding Neck Flange, Pipe Flange, Hydraulic Flange, Stainless Steel Flange |
Application: | Petroleum, Chemical, Fittings And Connection, Beer, Etc. | Pressure: | Class 150/300/600/900/1500/2500, PN 2.5/6/10/16/25/40, 0-63MPa, 150LB-2500LB |
Type: | Treaded Flange, Slip On Flange, Socket Weld Flange, Weld Neck Flange, Lap Joint Flange | Name: | Steel Flanges |
Process: | Forged, Drilling/Bending/Stamping, Heating Treament | Surface Treatment: | Heat Treament, Pickeling, Galvanized, Customize |
Inspection: | Mechinical Property Inspection, Factory Or Third Party Assigned, 100% Inspection | Connection: | Welding, Pipe And Pipe, Flange |
Material Grade: | 904L, UNS N08904 | Non Destructive Test: | Ultrsonic Test -ASTM E213, MT, PT |
Seal: | Raised Face | Manufacture: | Hot Forging / Rolling / Machining |
Connection Type: | Welded/Threaded/Flanged | Flange Type: | WN, LWN, SO, BL, SW |
Color: | On Quest,Natural Color,Black | Payment Term: | T/T, L/C, Western Union, Etc. |
Face: | FF,RF,RTJ,RING | Flange Facing Type: | Raised Face/Flat Face/Ring Type Joint |
High Light: | ASTM A182 F904L Neck Flange,Face Forged Long Welding Neck Flange,Petroleum Long Welding Neck Flange |
Flange types include lap joint, socket weld, weld neck and UNS N08904 blind flanges. Blind flanges close the pipeline. There are different types of blind flanges for different applications. Stainless steel 904L pipe flanges have a minimum tensile strength of 490MPa and a minimum yield strength of 220MPa. Flanges come in different sizes ranging from ½" to 48". The pressure rating of the flange varies by size. These flanges are available in pressure classes 150 to 2500. 904l stainless steel flanges are available in different production types such as plate flanges, threaded, threaded or forged flanges. The surface type of the flange is also different, such as a flat convex surface and an annular connection surface. ANSI B16.5 SS 904L Pipe Flanges are used in power generation, heat exchangers, boilers, chemical, petrochemical, oil and gas, and petroleum industry applications.
Stainless steel 904l flanges are made of unstable austenitic stainless steel material. The composition of the material consists of 23% nickel, 19% chromium and carbon, silicon, copper, sulfur, manganese, phosphorus and 4% molybdenum. Flanges conform to ASTM A182 and ASTM A240 specifications. ASTM A182 F904L stainless steel flanges are highly corrosion resistant. They are particularly resistant to chloride ions, mild acids and oxidation. Therefore, these flanges can be used in sour water service, seawater, brackish water and marine applications.
ASTM A182 F904L flange definition
ASTM A182 is a standard specification for wrought stainless steel pipe flanges and stainless steel wrought fittings.
ASTM 182 is for pressure systems, including flanges, fittings, and similar parts conforming to a specified size or dimension standard such as the ASME Code.
ASTM A182 F904L Flange is an unstable austenitic stainless steel with low carbon content. This high-alloy stainless steel has copper added to improve its resistance to strong reducing acids such as sulfuric acid. 904L is non-magnetic and has excellent formability, toughness and weldability.
Stainless steel 904L flanges contain many expensive components such as molybdenum and nickel. Today, most applications using the 904L grade have been replaced by the lower cost duplex 2205 grade.
ASTM A182 F904L flanges are suitable for industrial, construction and transportation applications.
ASTM A182 F904L Flange Range
|
---|
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Cu | |
904L | min. max. |
- 0.02 |
- 2 |
- 1 |
- 0.045 |
- 0.035 |
19 23 |
4 5 |
23 28 |
1 2 |
Grade | Tensile Strength (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) | Brinell (HB) | ||||
904L | 490 | 220 | 36 | 70-90 typical | 150 |
Grade | Density (kg/m3) |
Elastic Modulus (GPa) |
Mean Co-eff of Thermal Expansion (µm/m/°C) | Thermal Conductivity (W/m.K) |
Specific Heat 0-100°C (J/kg.K) |
Elec Resistivity (nΩ.m) |
|||
0-100°C | 0-315°C | 0-538°C | At 20°C | At 500°C | |||||
904L | 7900 | 190 | 15 | - | - | 11.5 | - | 500 | 952 |