Name: ASME SB622 N10276(Hastelloy C276) DIN2.4819 Nickel Alloy Seamless Pipe
Brand: Yuhong Group Co.,Ltd
SKU: ASME SB622 UNS N10276 (C-276 / DIN2.4819 )
Price: 150000.00 USD
Availability: InStock

Yuhong Holding Group Co.,LTD

English

Home

Products

About Us

Factory Tour

Quality Control

Company News

Home Products Nickel Alloy Pipe

ASME SB622 N10276(Hastelloy C276) DIN2.4819 Nickel Alloy Seamless Pipe

Product Details:

Place of Origin:	China
Brand Name:	YUHONG
Certification:	ABS, GL, DNV, NK, PED, AD2000, GOST9941-81, CCS, ISO 9001-2008
Model Number:	ASME SB622 UNS N10276 (C-276 / DIN2.4819 )

Payment & Shipping Terms:

Minimum Order Quantity:	100kg
Price:	NEGOTIABLE
Packaging Details:	Ply-wooden Case /Iron Case/ Bundle with plastic Cap
Delivery Time:	Depends on Quantity
Payment Terms:	T/T, L/C
Supply Ability:	According To Client's Requirement

Contact Now

All Products

Stainless Steel Seamless Pipe (308)

Stainless Steel Seamless Tube (297)

Duplex Stainless Steel Pipe (132)

Duplex Stainless Steel Tube (33)

Needle Tube (134)

Fin Tube (672)

Heat Exchanger (20)

Heat Exchanger Tube (443)

Heat Exchanger Tube Bundle (40)

Heat Exchanger Tubesheet (117)

Heat Exchanger Baffle (37)

Air Cooler (9)

Pressure Vessel (4)

Stainless Steel Welded Pipe (58)

Stainless Steel Welded Tube (120)

Nickel Alloy Pipe (266)

Nickel Alloy Tube (92)

Copper Alloy Tube (240)

Alloy Steel Tube (204)

Titanium Tube (15)

Bright Annealed Tube (155)

Boiler Tube (151)

Steel Fitting (826)

Steel Flange (615)

Others (401)

Cladding Parts (7)

Detailed Product Description

Product Name:	Nickel Allly Seamless Pipe	Standard:	ASME SB622
Material:	Hastelloy C-276, N10276, DIN2.4819	Surface:	Pickled And Annealed, Bright Annealed, Polished
Type:	Coil,U Tube,staight	Application:	Boiler Pipe,Structure Pipe,Oil Pipe,Chemical Fertilizer Pipe,Fluid Pipe
Length:	Customized	End:	Plain End, Beveled End
Highlight:	ASTM B626 Hastelloy C276 Seamless Pipe , 2.4819 Hastelloy C276 Seamless Pipe , ASTM B622 Hastelloy C276 Tube

ASTM SB622 UNS N10276 (C-276 /DIN 2.4819 ) Hastelloy Seamless Pipe

Hastelloy C276 is a nickel-molybdenum-chromium super alloy with an addition of tungsten designed to have excellent corrosion resistance in a wide range of severe environments. The high nickel and molybdenum contents make the nickel steel alloy especially resistant to pitting and crevice corrosion in reducing environments while chromium conveys resistance to oxidizing media. The low carbon content minimizes carbide precipitation during welding to maintain corrosion resistance in as-welded structures. This nickel alloy is resistant to the formation of grain boundary precipitates in the weld heat-affected zone, thus making it suitable for most chemical process application in an as welded condition.

Although there are several variations of the Hastelloy nickel alloy, Hastelloy C-276 is by far the most widely used.

Alloy C-276 is widely used in the most severe environments such as chemical processing, pollution control,pulp and paper production, industrial and municipal waste treatment, and recovery of sour natural gas.

Characteristics

HASTELLOY C276 is one of the few alloys resistant to wet chloride gas, hypochlorite and chlorine dioxide solutions.
HASTELLOY C276 has exceptional resistance to strong solutions of oxidizing salts, such as ferric and cupric chlorides.
HASTELLOY C276 is not prone to grain boundary precipitation in the as welded condition and therefore suitable for many chemical process applications

Applications

Digesters and bleach plants in the paper industry.
Components exposed to sour gas.
Equipment for flue-gas desulfurisation plants.
Evaporators, heat exchangers, filters and mixers used in sulfuric acid environments.
Sulfuric acid reactors.
Organic chloride process equipment.
Equipment for processes utilizing halide or acid catalysts.

Some typical applications of HASTELLOY C276 include equipment components in chemical and petrochemical organic chloride processes and processes utilizing halide or acid catalysts. Other industry applications are pulp and paper (digesters and bleach areas), scrubbers and ducting for flue gas desulfurization, pharmaceutical and food processing equipment.

HASTELLOY C-276 is a nickel-chromium-molybdenum alloy with universal corrosion resistance unmatched by any other alloy. It has outstanding resistance to a wide variety of chemical process environments including ferric and cupric chlorides, hot contaminated mineral acids, solvents, chlorine and chlorine contaminated (both organic and inorganic), dry chlorine, formic and acetic acids, acetic anhydride, sea water and brine solutions and hypochlorite and chlorine dioxide solutions. Alloy C276 also resists formation of grain boundary precipitates in the weld heat affected zone making it useful for most chemical processes in the as-welded condition. It has excellent resistance to pitting and stress corrosion cracking.

HASTELLOY C276 sheet 0.044" thick in the heat-treated condition at 2050°F, rapid quenched, has an average olsen cup depth of 0.48". Alloy C-276 can be successfully fabricated by many methods. The alloy tends to work harden but with the proper care, the alloy is readily hot and cold formed. Complete information on welding, machining and forming is available

Chemical Requirements
	Ni	Cr	Mn	Mo	C	Si	Fe
Max %	Bal.	16.5	1.0	17.0	0.010	0.08	7.0
Min %		14.5		15.0			4.0

Mechanical Property Requirements
	Ultimate Tensile	Yield Strength (0.2% OS)	Elong. in 2 in. (50.8mm) or 4D min,%	R/A	Hardness
Min	100 KSi	41 KSi	40
Max
Min (Metric)	690 MPa	283 MPa
Max

Chart of Average Tensile Data At Temperatures

Specifications
Form	Standard
UNS	UNS N10276
Bar	ASTM B574 Din 17752
Wire
Sheet	ASTM B575 Din 17750
Plate	ASTM B575 Din 17750
Fitting	ASTM B366
Forging	ASTM B564
Tube	ASTM B619 ASTM B622 ASTM B626 Din 17751
Pipe	ASTM B619 ASTM B622 ASTM B626 Din 17751
Weld Wire	A5.14 ERNiCrMo-4
Weld Electrode	A5.11 ENiCrMo-4
Din.	2.4819 All Forms

Table 16
RECOMMENDED TOOL TYPES AND MACHINING CONDITIONS
Operations	Carbide Tools
Roughing, with severe interruption	Turning or Facing C-2 and C-3 grade: Negative rake square insert, 45 degree SCEA1, 1/32 in. nose radius. Tool holder: 5 degree neg. back rake, 5 degree neg. side rake. Speed: 30-50 sfm, 0.004-0.008 in. feed, 0.150 in depth of cut. Dry2, oil3, or water-base coolant4.
Normal roughing	Turning or Facing C-2 or C-3 grade: Negative rate square insert, 45 degree SCEA, 1/32 in nose radius. Tool holder: 5 degree neg. back rake, 5 degree neg. side rake. Speed: 90 sfm depending on rigidity of set up, 0.010 in. feed, 0.150 in. depth of cut. Dry, oil, or water-base coolant.
Finishing	Turning or Facing C-2 or C-3 grade: Positive rake square insert, if possible, 45 degree SCEA, 1/32 in. nose radius. Tool holder: 5 degree pos. back rake, 5 degree pos. side rake. Speed: 95-110 sfm, 0.005-0.007 in. feed, 0.040 in. depth of cut. Dry or water-base coolant.
Rough Boring	C-2 or C-3 grade: If insert type boring bar, use standard positive rake tools with largest possible SCEA and 1/16 in. nose radius. If brazed tool bar, grind 0 degree back rake, 10 degree pos. side rake, 1/32 in. nose radius and largest possible SCEA. Speed: 70 sfm depending on the rigidity of setup, 0.005-0.008 in. feed, 1/8 in. depth of cut. Dry, oil or water-base coolant.
Finish Boring	C-2 or C-3 grade: Use standard positive rake tools on insert type bars. Grind brazed tools as for finish turning and facing except back rake may be best at 0 degrees. Speed: 95-110 sfm, 0.002-0.004 in feed. Water-base coolant.
Notes:
1 SCEA - Side cutting edge angle or lead angle of the tool. 2 At any point where dry cutting is recommended, an air jet directed on the tool may provide substantial tool life increases. A water-base coolant mist may also be effective. 3 Oil coolant should be premium quality, sulfochlorinated oil with extreme pressure additives. A viscosity at 100 degrees F from 50 to 125 SSU. 4 Water-base coolant should be premium quality, sulfochlorinated water soluble oil or chemical emulsion with extreme pressure additives. Dilute with water to make 15:1 mix. Water-base coolant may cause chipping and rapid failure of carbide tools in interrupted cuts.

Table 17
RECOMMENDED TOOL TYPES AND MACHINING CONDITIONS
Operations	Carbide Tools
Facing Milling	Carbide not generally successful, C- grade may work. Use positive axial and radial rake, 45 degree corner angle, 10 degree relief angle. Speed: 50-60 sfm. Feed: 0.005-0.008 in. Oil or waterbase coolants will reduce thermal shock damage of carbide cutter teeth.
End Milling	Not recommended , but C-2 grades may be successful on good setups. Use positive rake. Speed: 50-60 sfm. Feed: Same as high speed steel. Oil or water-base coolants will reduce thermal shock damage.
Drilling	C-2 grade not recommended, but tipped drills may be successful on rigid setup if no great depth. The web must thinned to reduce thrust. Use 135 degree included angle on point. Gun drill can be used. Speed: 50 sfm. Oil or water-base coolant. Coolant-feed carbide tipped drills may be economical in some setups.
Reaming	C-2 or C-3 grade: Tipped reamers recommended, solid carbide reamers require vary good setup. Tool geometry same as high speed steel. Speed: 50 sfm. Feed: Same as high speed steel.
Tapping	Not recommended, machine threads, or roll-form them.
Electrical Discharge Machining	The alloys can be easily cut using any conventional electrical discharge machining system (EDM) or wire (EDM).
Notes:
5 M-40 series High Speed Steels include M-41 , M-42, M-43, M-44, M-45 and M-46 at the time of writing. Others may be added and should be equally suitable. 6 Oil coolant should be a premium quality, sulfochlorinated oil with extreme pressure additives. A viscosity at 100 degree F from 50 to 125 SSU. 7 Water-base coolant should be premium quality, sulfochlorinated water soluble oil or chemical emulsion with extreme pressure additives. Dilute with water to make 15:1 mix.

Table 18
Plasma Arc Cutting
Our alloys can be cut using any conventional plasma arc cutting system. The best arc quality is achieved using a mixture of argon and hydrogen gases. Nitrogen gas can be substituted for hydrogen gases, but the cut quality will deteriorate slightly. Shop air or any oxygen bearing gases should be avoided when plasma cutting these alloys.