ASTM A312 S31254 Duplex Stainless Steel Welded Pipe For Offshore Application

ASTM A312 S31254 Duplex Stainless Steel Welded Pipe For Offshore Application

  • ASTM A312 S31254 Duplex Stainless Steel Welded Pipe For Offshore Application
  • ASTM A312 S31254 Duplex Stainless Steel Welded Pipe For Offshore Application
  • ASTM A312 S31254 Duplex Stainless Steel Welded Pipe For Offshore Application
ASTM A312 S31254 Duplex Stainless Steel Welded Pipe For Offshore Application
Product Details:
Place of Origin: China
Brand Name: Yuhong
Certification: ABS, BV, ISO, ASTM, SGS
Model Number: ASTM A312 S31254
Payment & Shipping Terms:
Minimum Order Quantity: 100kgs
Price: Negotiable
Packaging Details: Ply-wooden case packing
Delivery Time: 7Days
Payment Terms: L/C, T/T
Contact Now
Detailed Product Description
Material: 254 SMo,1.4547, UNS 31254 ,1.4529, Z1 CNDU 20.18.06AZ Testing: Eddy Current Test , Hydrostatic Test , UT , PT
Appilcation: Chemical Industry , Heat Exchanger, Boiler, Offshore, Platform, Subsea Norsok: Norsok MDS R11/R18, IOGP S-563 MDS IR111/111S/IR118/IR118S
High Light:

ASTM A312 S31254 Welded Pipe

,

Offshore Stainless Steel Pipe

,

Offshore Duplex Stainless Steel Tube

 

ASTM A312 S31254 Duplex Stainless Steel Welded Pipe For Offshore Application

 

ASTM A312 S31254 Stainless Steel Seamless Pipe , offshore and platform application

 

254 SMO is a high-alloy austenitic stainless steel developed for use in seawater and other aggressive chloride-bearing media. The steel is characterized by the following properties:

 

  • A.Excellent resistance to pitting and crevice corrosion, PRE = ≥42.5%
  • B.High resistance to general corrosion
  • C.High resistance to stress corrosion cracking
  • D.Higher strength than conventional austenitic stainless steels
  • E.Good weldability

The PRE is defined as, in weight of content %, PRE = Cr % + 3.3 x Mo % + 16 x N %

 

 

Standards

  • UNS: S31254
  • EN Number: 1.4547
  • EN Name: X1CrNiMoCuN20-18-7
  • W.Nr.: 1.4529
  • SS: 2378
  • AFNOR: Z1 CNDU 20.18.06AZ

    Product standards
  • Seamless tube and pipe: ASTM A269, A213, A312, NFA 49-217, EN 10216-5
  • Norsok MDS R11/R18, IOGP S-563 MDS IR111/111S/IR118/IR118S
  • Welded tube and pipe: ASTM A249, A269 , A312, A358, A409
  • Fittings: ASTM A182
  • Bar: ASTM A276, A479, EN 10088-3
  • Forged products: ASTM A473
Chemical composition (nominal) %
C Si Mn P S Cr Ni Mo N Cu
≤0.020 ≤0.80 ≤1.00 ≤0.030 ≤0.010 20 18 6.1 0.20 0.7

254 SMO Applications:

  • 1. Equipment for handling of seawater, such as, seawater cooling, cooling water pipes, ballast water systems, firefighting systems etc.
  • 2. Hydraulic and instrumention tubing
  • 3. Equipment in pulp bleaching plants
  • 4. Components in gas cleaning systems
  • 5. Tanks and pipelines for chemicals with high halide contents
Stress corrosion cracking tests in boiling 25% NaCl solution, pH=1.5. U-bend specimens.
ASTM TP316
<150 h
Pitting
'904L'
No failure (1000 h)
Crevice corrosion
Sandvik 254 SMO
No failure (1000 h)
No attack
Grade Time to failure hours
Stress corrosion cracking tests. Drop evaporation method*. Stress: 0.9xRp0.2
ASTM TP316
105
TP904L
225
254 SMO
425

Intergranular corrosion

254 SMO has a very low carbon content. This means that there is very little risk of carbide precipitation during heating, for example when welding. The steel passes the Strauss test (ASTM A262, practice E) even after sensitizing for one hour at 600–1000°C (1110–1830°F).

However, due to the high alloying content of the steel, inter-metallic phases can precipitate at the grain boundaries in the temperature range 600–1000°C (1110–1830°F). These precipitations do not involve any risk of intergranular corrosion in the environments in which the steel is intended to be used. Thus, welding can be carried out without any risk of intergranular corrosion.

Pitting corrosion

The pitting and crevice corrosion resistance of stainless steel is primarily determined by the content of chromium, molybdenum and nitrogen. Manufacture and fabrication, e.g. welding, are also of vital importance for the actual performance in service. A parameter for comparing the resistance to pitting in chloride environments is the PRE number (Pitting Resistance Equivalent). The PRE is defined as, in weight-%, PRE = %Cr + 3.3 x %Mo + 16 x %N

Heat Treatment
The tubes are delivered in heat treated condition. If additional heat treatment is needed due to further processing the following is recommended.
Solution annealing 1150–1200°C (2100–2190°F), quenching in water. Thin-walled tubes min. 1130°C (2060°F), quenching in air/water.

Mechanical Properties
 
Wall thickness Proof strength Tensile strength Elong. Hardness
  Rp0.2a) Rp1.0a) Rm Ab) A2" HRB
mm MPa MPa MPa % %  
Metric units, at 20°C
<5 ≥310 ≥340 675-850 ≥35 ≥35 ≤96
>5 ≥310 ≥340 655-850 ≥35 ≥35 ≤96
1 MPa = 1 N/mm2

 

Wall thickness Proof strength Tensile strength Elong. Hardness
  Rp0.2a) Rp1.0a) Rm Ab) A2" HRB
inch ksi ksi ksi % %  
Imperial units, at 68°F
<0.187 ≥45 ≥49 98-123 ≥35 ≥35 ≤96
>0.187 ≥45 ≥49 98-123 ≥35 ≥35 ≤96

a) Rp0.2 and Rp1.0 correspond to 0.2% offset and 1.0% offset yield strength, respectively.
b) Based on L0 = 5.65 √S0 where L0 is the original gauge length and S0 the original cross-section area.

 

Weldding:

Recommended filler metals

TIG/GTAW or MIG/GMAW welding
ISO 18274 S Ni 6625/AWS A5.14 ERNiCrMo-3 (e.g. Exaton Ni60)
ISO 18274 S Ni 6059/AWS A5.14 ERNiCrMo-13 (e.g. Exaton Ni59)

MMA/SMAW welding
ISO 14172 E Ni 6625/AWS A5.11 ENiCrMo-3 (e.g. Exaton Ni60)
ISO 14172 E Ni 6059/AWS A5.11 ENiCrMo-13 (e.g. Exaton Ni59)

ASTM A312 S31254 Duplex Stainless Steel Welded Pipe For Offshore Application 0

Contact Details
Yuhong Group Co.,Ltd

Contact Person: Ms Sia Zhen

Tel: 15058202544

Send your inquiry directly to us (0 / 3000)